Verifying my load.

Discussions of powders, bullets and loading information.

Moderators: Kirk, Lucinda

amprat
Posts: 26
Joined: Wed Oct 13, 2021 6:53 pm

Re: Verifying my load.

Post by amprat »

Kenny Wasserburger wrote: Fri Dec 10, 2021 12:08 pm Loose the Lyman #2 Alloy. Get a good lead tin alloy, start at 20-1. Binary alloys….you can thank us later.


Kenny Wasserburger
Please explain why, casting is new to me. I had been under the impression that a softer mix would cause leading, and thought #2 should help avoid it.
User avatar
JonnyV
Posts: 547
Joined: Mon Jun 28, 2021 3:52 pm
Location: Living in a van down by the river eatin’ Govt cheese
Contact:

Re: Verifying my load.

Post by JonnyV »

Leading is caused more by improper bullet fit with the bore than by hardness. You can have a very successful bullet with a soft alloy. Increasing hardness is normally the avenue taken by commercial casters because their bullets need to fit a wide variety of different chamberings and bore diameters.

This book covers the basics of casting. It's free for you to use/print off on your home computer.

http://www.lasc.us/Fryxell_Book_Contents.htm
Kenny Wasserburger
Posts: 4728
Joined: Tue Sep 24, 2002 3:53 pm
Location: Gillette, Wyoming

Re: Verifying my load.

Post by Kenny Wasserburger »

Your thinking is wrong, I won’t spend time to try and convince you.

The most successful shooters in this game are using binary alloys of lead and tin, anywhere from 1-12 to 1-20. Tin to lead. Both in paper patched and grease groove. This comes from years of experience and tens of thousands of rounds down range.

You have been good honest information, it’s now in your ball court as what you choose to do.


Kenny Wasserburger
We'll raise up our Glasses against Evil Forces, Singing, Whiskey for my men, Beer for my horses.

Wyoming Territory Sharps Shooter
TGC
Posts: 40
Joined: Mon Dec 23, 2019 12:57 pm

Re: Verifying my load.

Post by TGC »

Good word Kenny. It make sense to start with a proven alloy. Thank you for opening my eyes. Merry Christmas. Tim.
amprat
Posts: 26
Joined: Wed Oct 13, 2021 6:53 pm

Re: Verifying my load.

Post by amprat »

Why is antimony to be avoided?
User avatar
JonnyV
Posts: 547
Joined: Mon Jun 28, 2021 3:52 pm
Location: Living in a van down by the river eatin’ Govt cheese
Contact:

Re: Verifying my load.

Post by JonnyV »

I'm a stone cold rookie with this, but I think it has to do with the way that antimony hardens the lead...something about the chemical structure of the resulting alloy.

When we shoot a round of BP ammo, we need the bullet to obturate. It shortens just a little amount, caused by the near instantaneous burning of all the BP present. This super fast burn curve is so sudden that the bullet can't move fast enough and the bullet gets a little bit fatter as a result. This makes for a great fit with the bore, and very fine accuracy can be achieved as a result. Hardened alloys don't work as well for this, and antimony alloys can be brittle as well. That's the last thing you need.

For a long time, I mined the berms at my local club for lead and smelted it down. That's great for cranking out a bunch of 9mm and 38 and 44 bullets, but it's not great for long range rifle shooting. There reason is that its an unknown alloy, and bullets from one casting session may not shoot the same as bullets from another casting session. Now, my rifles don't see anything but 20-1 from John Walters in Oklahoma. His number is (405) 799-0376. Prices are right, and he ships flat rate. Really good guy. Do yourself a huge favor and go with a known, two part alloy.

Others more knowledgeable than myself may come by and correct anything I messed up here or add other things I might have missed, but I think I'm directionally correct.
semtav
Posts: 2876
Joined: Wed Feb 03, 2010 3:21 pm
Location: Montana

Re: Verifying my load.

Post by semtav »

And then there's the "Quigley" alloy. But prob best not to delve into that quagmire.
User avatar
Don McDowell
Posts: 7633
Joined: Thu Nov 29, 2007 2:04 pm
Location: Ft. Laramie Wy
Contact:

Re: Verifying my load.

Post by Don McDowell »

Higher antimony content tends to age harden. If you cast say the #2 up and shoot it right away if the rifle likes it and the load you'll be fine. But if you do a batch of say 4-500 ahead of a shooting season, you'll run into some weird misses or shots not running to call at the longer distances... :oops: Don't ask me how I found that out... :lol:
20-1 works well for most bpcr bullets especially at distances under 600, beyond that nose slump can have some bad affects beyond 800.
16-1 will shoot consistently from powder burn close to the 1000 yd and further, and some are having great success with 12 and 14-1.
18-1 is another pretty decent choice and you can make it up by simply combining equal amounts of 20-1 and 16-1 in the pot. The problem comes if you don't completely empty the pot you may end up with something of a lopsided alloy. So therefore I think its best if buying premixed alloy to pick one and stick with it.
AKA Donny Ray Rockslinger :?
Kurt
Posts: 8428
Joined: Wed Oct 12, 2005 10:28 pm
Location: Not Far enough NW in Illinois

Re: Verifying my load.

Post by Kurt »

I'm an Advocate of using antimony in my bullet alloy.
When a bullet leaves the muzzle looking like these in the photo's and they don't hit center it's not the fault of the alloy.
I know a shooter that uses a mix of WW and Linotype and seen him shoot a 99 with one just in the 9 ring less than a 1/2" at 800 yards. That is a very rich mix of antimony.

These bullets were shot in a .45-70, .45-90, .44-77 and a .40-65
IMG_2276.JPG
IMG_3529.JPG
IMG_3334.JPG
The reason a dog has so many friends is because he wags his tail instead of his tongue.

"Socialism is a philosophy of failure, the creed of ignorance, and the gospel of envy, its inherent virtue is the equal sharing of misery"Winston Churchill
User avatar
bpcr shooter
Posts: 800
Joined: Sun Feb 04, 2018 5:30 pm
Location: Madison, Wi

Re: Verifying my load.

Post by bpcr shooter »

Im with you Kurt! Ive switched to the 17+1 and it works very well. No rifling past the patch line. Ive used that WW+Lino in my 38-55 and with SPG lube I've had zero leading and it shoots very well!

If I remember correctly that 800yd score is yet to be beat at Lodi, it was a 40-65 to boot.
NMLRA Member
Winnequah Gun Club Member (Lodi, Wi)
WIFORCE Member
SCI Member
rgchristensen
Posts: 180
Joined: Sat Jan 16, 2016 10:51 pm

Re: Verifying my load.

Post by rgchristensen »

My impression of "custom casters" is that they will make bullets out of anything they can melt.

CHRIS
beltfed
Posts: 1962
Joined: Sun Jun 03, 2007 10:07 am
Location: Central Wi

Re: Verifying my load.

Post by beltfed »

Yes, who says that antimony alloys don't shoot. My ww/lino alloy,
estimated at about 94.5% lead, 4.5% antimony,1% tin
beltfed/arnie
IMG_1459.JPG
You do not have the required permissions to view the files attached to this post.
beltfed
Posts: 1962
Joined: Sun Jun 03, 2007 10:07 am
Location: Central Wi

Re: Verifying my load.

Post by beltfed »

The key to shooting hard, antimony containing bullets is the base bands diameter has to be at freebore/groove to plus 1 or 2 thou.
So, they do not have to "bump up".
Kenny, note how your DDEPP bullet fits. I know that 16+1 works with them.
But, You could use hard, absolutely non slumping bullets, though,
too.
beltfed/arnie
Kenny Wasserburger
Posts: 4728
Joined: Tue Sep 24, 2002 3:53 pm
Location: Gillette, Wyoming

Re: Verifying my load.

Post by Kenny Wasserburger »

Arnie,

Currently I am using a alloy to get that 16-1 using soldier that Kurt mentioned from 20-1 down to 16-1 it has shown promise but my antimony content is in the final mix less than 1%. Ian has tried up to 5% with his patched to bore bullets, yet has decided to cut back. I honestly think it can be too much of a good thing.

Kenny
We'll raise up our Glasses against Evil Forces, Singing, Whiskey for my men, Beer for my horses.

Wyoming Territory Sharps Shooter
Kenny Wasserburger
Posts: 4728
Joined: Tue Sep 24, 2002 3:53 pm
Location: Gillette, Wyoming

Re: Verifying my load.

Post by Kenny Wasserburger »

Arnie,

Currently I am using a alloy to get that 16-1 using soldier that Kurt mentioned from 20-1 down to 16-1 it has shown promise but my antimony content is in the final mix less than 1%. Ian has tried up to 5% with his patched to bore bullets, yet has decided to cut back. I honestly think it can be too much of a good thing.

Kenny
We'll raise up our Glasses against Evil Forces, Singing, Whiskey for my men, Beer for my horses.

Wyoming Territory Sharps Shooter